Technical Parameter For Extruder MachineBase Material1)38CrMoAlA(JIS SACM645);2)Cr12MOV(JIS SKD-11) ;
3)4Cr5MoSiV1(JIS SKD-61) ;4)42CrMo(AISI 4140) Bimetallic Alloy Materials1)Fe-based alloy  2)Ni-based alloy/Deloro alloy 
3)Co-based alloy  4)NiCo-based alloy 
5)Tungsten carbide/Wolfram carbide Double-alloy levelLevel A - containing Tungsten of 40%
Level B - containing tungsten of 25%
Level C - containing tungsten of 9.5%Surface  TreatmentHeat Treatment
High Frequency Treatment
Nitriding treatment(120 Hours):
Depth of Nitrided Layer: 0.5-0.8 mm
Hardness of Nitrided Layer: 900-1020Hv (HRC56°-65°)
Hard Chrome Plating treatment:
Thickness of Hard Chrome Plating Layer: 0.05-0.10mm
Hardness of Hard Chrome Plating Layer:  ≥ 950HV
Nickel alloy plating.treatment:
Bimetallic Barrel/Cylinder: Centrifugal Casting (Inlay Alloy)
Bimetallic Screw: Plasma Alloy Coating Spraying
Depth of Bimetallic Layer: >2mm
Hardness of Bimetallic Layer: HRC55°-72°
Spraying corrosion wear-resisting dual metal layersBasic informationRoughness of the surface:Ra0.4um
Linearity of the screw:  ≤ 0.015mm
Linear axis limit:  ≤ 0.02mm
Hardness after Hardening & Tempering: HB240-280
Fragility of Nitration: ≤ Two classMaterial Application1)General Plastics
2)ABS,PA,PC,PE,PET,PP,PS,EVA,PU,PVC,U-PVC,etc
3)PA + GF(Glass Fiber)
4)Flame-resistant Reinforced Plastics
5)Modified Engineering Plastics
6)All kinds of Mixed Recycled Material(in Scrap or Granule), PVC + 30% CaCo3, etc